Photopolymer

Nyloflex® Seal F | Nyloflex® Seal F Digital

Polymers form the basis of flexographic printing quality

Nyloflex^® Seal F

Base material

Colour of raw plate

Total thickness2 (mm) (inch)

Hardness acc. to DIN 53505 (Shore A)

Plate hardness (Shore A)

Relief depth (mm)

Tonal range (%) at screen ruling (l/cm)

Fine line width (down to μm)

Isolated dot diameter (down to μm)

Elongation constant (mm)

Back exposure (s)

Main exposure (min)

Washout speed (mm/min)

Drying time at 60°C / 140°F (h)

Post exposure UV-A (min)

Light ﬁ nishing UV-C (min)4

116

Polyester foil

violet

1.16 (0.046“)

36

72

0.9

3 – 90 | 48 l/cm (122 lpi)

300

750

5.72

10-12

10-15

100-130

2

10

10-15

116

Polyester foil

violet, with black LAMS layer

1.16 (0.046“)

36

72

0.9

2 – 95 | 48 l/cm (122 lpi)

300

750

5.72

10-12

8-12

100-130

2

10

10-15

Equipment Technology Photopolymer Quality control Occupational safety and health

Advantages of nyloflex® Seal F Digital

higher printing quality with sharper images and more open intermediate depths
increased productivity, reduced failure rate and data transfer without loss of quality due to a digital workflow
consistency in quality at repeated plate processing
cost-effective and more environmentallyfriendly in processing as no film is required